TM 43-0139 Table 3-4.  Non-Camouflage Finish Systems Type Surface Pretreatment Primer Coats Intermediate Coats Finish¹¹ Coats¹ A Metal DOD-P-15328⁴ TT-E-485 1 - - TT-E-485 1 TT-P-636 Metal (For lead and DOD-P-15328⁴ 1 - - TT-E-529^1,2,3 1 chromate free) Metal (For marine DOD-P-15328 TT-P-645 1 - - TT-E-485 2 environment) TT-E-1593 Wood (For lead and See MIL-T-704 TT-P-636 1 - - TT-E-529 1 chromate free) See MIL-T-704¹⁰ TT-E-529^1,2,3 1 B Metal - MIL-P-24441, 1 MIL-P-24441, 1 MIL-P-24441, 1 (B-1¹³) formula 150 formula 150 formula as specified (B-2¹⁴) - MIL-P-24441, 1 MIL-P-24441, 2 MIL-P-1 5931 2 formula 150 formula 150 Wood See MIL-T-704 TT-P-636 1 1 TT-P-636 1 TT-E-522 1 C Metal DOD-P-15328⁴ - - - TT-E-485^3,9 1 D Metal DOD-P-15328⁴ TT-P-1757⁶ 1 - - TT-E-529¹ 2 E Metal DOD-P-15328⁴ TT-P-1757⁶ 1 - - MIL-L-52043 2 F Ferrous metal DOD-P-15328⁴ 1 - - MIL-C-22750⁸ 2 MIL-P-53022¹² MIL-C-46168⁸ MIL-P-53030¹² MIL-C-53039⁸ G Non-ferrous metal DOD-P-15328⁴ MIL-P-23777¹² 1 - - MIL-C-22750⁸ 2 MIL-P-53022¹² MIL-C-46168⁸ MIL-P-53030¹² MIL-C-53039^{8 1}For vehicles or equipment specified in MIL-T-704, paragraph 3.3.4.5, coat shall conform to TT-E- 489 ²A maximum of five percent of chrome yellow, TT-P-381, color 7B, shall be added to enamel, TT-E- 485, when it is used as a primer, or the black may be omitted and the resulting yellow enamel used as the primer so as to provide a color contrast between coats.  The yellow enamel with the black omitted shall be used as the primer when the color of the finish coat is other than forest green or dark green.  Gloss finish coats shall conform to TT-E-489. ³When paint conforming to TT-E-485 is used, the type shall be suited to the method of application. ⁴Altemates specified in MIL-T-704, paragraph 3.2, can be used interchangeably with DOD-P-15328. ⁵TT-E-485 or equal commercial primer. ⁶Color optional. ⁷Camouflage coatings must conform to MIL-T-704, paragraph 3.3.4.1 ,except that camouflage coatings applied over type C finishes must also be compatible with the under coatings used. ⁸For use where chemical agent resistance is required, or for greater durability. ⁹When using this finish and requiring the camouflage forest green color, an anticorrosive primer must be used. ¹⁰When lacquer resistance is required, TT-E-485, type IV, or TT-P-664 can be used.  When camouflage painting is required, the camouflage and coatings shall replace these specified topcoats (See table 3-3). ¹²Parts and components may first be primed with alkyd base primer, which has been allowed to cure for a minimum of 15 days, and then cleaned and primed as specified herein either prior to or at final end item assembly painting. ¹³For general use for water immersion and salt air exposure. ¹⁴For continuous use in sea water; not for salt air exposure. Change 3     3-11